Germany DIN Special Alloy GS-38NiCrMo8 4 4,及該型號鋼材的基本信息、化學元素成分、機械性能、力學性能、熱處理溫度、同等型號參照表等。
Germany DIN Special Alloy GS-38NiCrMo8 4 4,及該型號鋼材的基本信息、化學元素成分、機械性能、力學性能、熱處理溫度、同等型號參照表等。
分類 | 種類 | 型號 | 標準 | 國家 | 應用 |
---|---|---|---|---|---|
Steel Grades | GS-38NiCrMo8 4 4 | DIN | Germany |
元素名稱 | 含量比例值 |
---|---|
C | 0.35-0.40 |
Si | 0.40-0.60 |
Mn | 0.40-0.60 |
P | Max 0.035 |
S | Max 0.035 |
Cr | 0.90-1.20 |
Ni | 1.90-2.20 |
Mo | 0.40-0.50 |
屈服強度Rp0.2(MPa) | 抗拉強度Rm(MPa) | 沖擊率 | 伸長率 | 斷面收縮率 | 熱處理狀態(tài) | 布氏硬度(HBW) |
---|---|---|---|---|---|---|
512 (≥) | 284 (≥) | 31 | 21 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 121 |
溫度 | 彈性模量 | 系數(shù) | 熱導率 | 比熱容量 | 比電阻率 | 密度 | 加權(quán)系數(shù) |
---|---|---|---|---|---|---|---|
41 | - | - | 0.23 | - | |||
417 | 541 | - | 22.3 | 423 | - | ||
261 | - | 43 | 33.2 | 332 | 241 |
熱處理溫度區(qū)間 |
---|
Heat treated : 1193°C - 1923°C |
型號 | 標準 | 國家 | 應用 |
---|---|---|---|
GS-38NiCrMo8 4 4 | DIN | Germany | |
Q195 | GBT | China | China structural steel and alloy steel |
Q215 | GBT | China | China structural steel and alloy steel |
Q215 B | China | Engineering and welding | |
Q235 | GBT | China | China structural steel and alloy steel |
Q235 B | China | Engineering and welding | |
Q235 C | China | Engineering and welding | |
Q235 D | China | Engineering and welding | |
Q255 A | China | Engineering and welding | |
Q255 B | China | Engineering and welding | |
Q275 | GBT | China | China structural steel and alloy steel |
Q235q C | China | Bridge structure with steel | |
Q235q D | China | Bridge structure with steel | |
Q345q E | China | Bridge structure with steel | |
Q345q C | China | Bridge structure with steel | |
ASTM 1030 | ASTM | USA | General use carbon steel bar |
UNS G10300 | UNS | USA | General use carbon steel bar |
ASTM 1005 | ASTM | USA | General use carbon steel bar |
UNS G10050 | UNS | USA | General use carbon steel bar |
ASTM 1006 | ASTM | USA | General use carbon steel bar |