USA ASTM Special Alloy CN-7M,及該型號鋼材的基本信息、化學(xué)元素成分、機(jī)械性能、力學(xué)性能、熱處理溫度、同等型號參照表等。
USA ASTM Special Alloy CN-7M,及該型號鋼材的基本信息、化學(xué)元素成分、機(jī)械性能、力學(xué)性能、熱處理溫度、同等型號參照表等。
分類 | 種類 | 型號 | 標(biāo)準(zhǔn) | 國家 | 應(yīng)用 |
---|---|---|---|---|---|
Steel Grades | CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
元素名稱 | 含量比例值 |
---|---|
C | 0.0700000000000000 |
Si | 1.5 |
Mn | 1.5 |
P | 0.04 |
S | 0.04 |
Cr | 19.0-22.0 |
Ni | 27.0-30.0 |
Mo | 2.0-3.0 |
屈服強(qiáng)度Rp0.2(MPa) | 抗拉強(qiáng)度Rm(MPa) | 沖擊率 | 伸長率 | 斷面收縮率 | 熱處理狀態(tài) | 布氏硬度(HBW) |
---|---|---|---|---|---|---|
641 (≥) | 245 (≥) | 21 | 23 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
溫度 | 彈性模量 | 系數(shù) | 熱導(dǎo)率 | 比熱容量 | 比電阻率 | 密度 | 加權(quán)系數(shù) |
---|---|---|---|---|---|---|---|
41 | - | - | 0.22 | - | |||
877 | 722 | - | 13.3 | 311 | - | ||
479 | - | 22 | 21.2 | 314 | 224 |
熱處理溫度區(qū)間 |
---|
Heat treated : 1188°C - 1833°C |
型號 | 標(biāo)準(zhǔn) | 國家 | 應(yīng)用 |
---|---|---|---|
CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7MS | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
ASTM CN-7M | AISI | USA | |
ASTM CN-7MS | AISI | USA | |
CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7MS | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7MS | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7MS | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7M | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |
CN-7MS | ASTM | USA | Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service |